Objective To prepare silver-containing hydroxyapatite coating (hydroxyapatite/Ag, HA/Ag) and investigate its antibacterial property and biocompatibil ity in vitro. Methods Vacuum plasma spraying technique was adopted to prepare HA/Ag coating on titanium alloy substrate (3% Ag). After incubating the HA/Ag and the HA coating under staphylococcus aureus and pseudomonas aeruginosa suspensions of 2% tryptic soy broth (TBS) medium for 2, 4 and 7 days, respectively, the biofilm on the coatings was examined by confocal laser scanning microscope, and the bacterial density and viable bacterial percentage of bacterial biofilm were calculated. Meanwhile, the micro-morphology of bacterial biofilm was observed by SEM, the cytotoxicity was detected via MTT and the biocompatibil ity of biofilm was evaluated by acute aemolysis test. Results Compared with HA coating, the bacterial biofilm’s thickness on the surface of HA/Ag coating witnessed no significant difference at 2 days after culture (P gt; 0.05), but decreased obviously at 4 and 7 days after culture (P  lt; 0.01). The bacterial density of the biofilm increased with time, but there was no significant difference between two coatings (P  gt; 0.05) at 2, 4 and 7 days after culture. The viable bacterial percentage of the biofilms on the surface of HA/Ag coating decreased obviously compared with that of HA coating at 2, 4 and 7 days after cultureP  lt; 0.01). The MTT notified the cytotoxic grade of both coatings was zero. The acute haemolysis assay showed that the hemolytic rate of HA/Ag and HA coating was 0.19% and 0.12%, respectively. Conclusion With good biocompatibil ity, significant antibacterial property against staphylococcus aureus and pseudomonas aeruginosa, no obvious cytotoxicity and no erythrocyte destruction, the vacuum plasma sprayed HA/Ag coating is a promising candidate for the surface of orthopedic metal implants to improve their osseointegration and antibacterial property.

Citation: RUAN Hongjiang,LIU Junjian,FAN Cunyi,ZHENG Xuebin,CHEN Yikai. EXPERIMENTAL RESEARCH IN VITRO ON ANTIBACTERIAL PROPERTY AND BIOCOMPATIBILITY OF ILVERCONTAINING HYDROXYAPATITE COATING. Chinese Journal of Reparative and Reconstructive Surgery, 2009, 23(2): 226-230. doi: Copy

Copyright © the editorial department of Chinese Journal of Reparative and Reconstructive Surgery of West China Medical Publisher. All rights reserved