Objective To investigate the possibility of creation of tissue engineered heart valve leaflets in vitro . Methods Aorta were obtained from 9 hybrid young pigs. The endothelial cell, fibroblast and smooth muscle cells were isolated and cultured to get enough cell. The expanded fibroblast, smooth muscle cell,and endothelial cells were seeded on the polymers sequentially. The cell polymer constructs were sent for scanning electron microscopy(SEM) examination after cultured for 7, 14, and 28 days. Histological examination were performed after the cell polymer constructs cultured for 28 days. Results SEM showed that the number of cells on the polymers increased as the culture time prolonged, with the formation of matrix. After 28 days, there were a great number of cells and large amount of matrix on the scaffolds. The confluent cell had covered a large area of the polymers. Hematoxylin and eosin(HE) stain showed large amount of cells attached to the polymers. Conclusion With the viability of the cultured cellular scaffolds,it is possible to create tissue engineered heart valve leaflets in vitro.
Objective To investigate the possible mechanism of the fibroblasts inducing the vascularization of dermal substitute. Methods Fibroblasts were seeded on the surface of acellular dermal matrix and cultivated in vitro to construct the living dermal substitute. The release of interleukin 8 (IL 8) and transfonming growth factor β 1(TGF β 1) in culture supernatants were assayed by enzyme linked immunosorbent assay, the mRNA expression of acid fibroblast growth factor (aFGF) and basic fibroblast growth factor (bFGF) were detected by RT-PCR. Then, the living substtute was sutured to fullth ickness excised wound on BALBouml;C m ice, and the fate of fibroblast w as observed by using in situ hybridizat ion. Results Fibroblasts cultured on acellular dermalmat rix p ro liferated and reached a single2layer confluence. Fibroblasts could secret IL 28 (192. 3±15. 9) pgouml;m l and TGF-B1 (1. 105±0. 051) pgouml;m l. There w as the mRNA exparession of aFGF and bFGF. Fibroblasts still survived and proliferated 3 weeks after graft ing. Conclusion Pept ides secreted by fibroblasts and its survival after graft ing may be relat ive to the vascularizat ion of the dermal subst itute.
Objective To review the latest development in the research on the application of the electrostatic spinning technology in preparation of the nanometer high polymer scaffold. Methods The related articles published at home and abroad during the recent years were extensively reviewed and comprehensively analyzed. Results Micro/nano-structure and space topology on the surfaces of the scaffold materials, especially the weaving structure, were considered to have an important effect on the cell adhesion, proliferation, directional growth, and biological activation. The electrospun scaffold was reported to have a resemblance to the structure of the extracellular matrix and could be used as a promising scaffold for the tissue engineeringapplication. The electrospun scaffolds were applied to the cartilage, bone, blood vessel, heart, and nerve tissue engineering fields. Conclusion The nanostructured polymer scaffold can support the cell adhesion, proliferation, location, and differentiation，and this kind of scaffold has a considerable value in the tissue engineering field.
OBJECTIVE: To explore the relationship between characteristics of transformed cell and tumorigenicity. METHODS: Documents about transformed cell and tumorigenicity were reviewed in detail. RESULTS: Normal biological characteristics and cell function could be maintained in non-tumorigenic transformed cell, but it was changed markedly in malignant transformed cell. CONCLUSION: Non-tumorigenic transformed cell can be served as a standard cell line to study the function and growth characteristics of normal cell.
OBJECTIVE To investigate the adhesive interactions of cells with materials and the effects of material properties on cell adhesion in tissue engineering. METHODS By looking up the recent literatures dealt with adhesive interactions of cells with materials and reviewing previous work on the adhesion of tissue-derived cells to materials. RESULTS The adhesion characteristics of cells to materials not only depend on the nature of materials, including bulk and surface properties, surface modification, surface morphology, net charge, porosity and degradation rate, but also on the expression of cell surface molecules and their interaction with the material. CONCLUSION The quantitative measure and biophysical mechanisms of cell adhesion to materials might be very important in tissue engineering.
OBJECTIVE: To investigate the biological characteristics of human muscle satellite cell cultured in vitro. METHODS: Human muscle satellite cells were obtained from skeletal muscle biopsies of six patients during corrective orthopedic surgery, cultivated in growth medium for ten days, then in differentiation medium for additional five days. Human satellite cells were identified with monoclonal antibody against desmin. Cells were observed under phase contrast microscopy. RESULTS: Human muscle satellite cells proliferated in growth medium, and fused to form myotubes in differentiation medium. After 24 hours in differentiation medium, the confluent satellite cells began to fuse actively and achieved the top level at 72 hours. CONCLUSION: Human muscle satellite cell can proliferate and differentiate in appropriate culture condition. Immunocytochemical detection of desmin is the effective early method to determine satellite cell.
OBJECTIVE To investigate the methods to fabricate repair materials of tissue engineered peripheral nerve with bioactivity of Schwann cells (SC). METHODS 1. The materials were made by dry-wet spinning process to fabricate PLA hollow fiber canal with external diameter of 2.3 mm, internal diameter of 1.9 mm, thickness of 0.4 mm, pore size of 20 to 40 microns, pore ratio of 70% and non-spinning fiber net with pore size of 100 to 200 microns, pore ratio of 85%. 2. SC were implanted into excellular matrix (ECM) gel to observe the growth of SC. 3. SC/ECM complex were implanted into non-spinning PLA fiber net to observe the growth of SC. 4. SC, SC/ECM and SC/ECM/PLA were implanted into PLA hollow fiber canal to bridge 10 mm defect of rat sciatic nerve. RESULTS 1. SC were recovered bipolar shape at 1 day after implantation, and could be survived 14 days in ECM gel. 2. After SC/ECM complex was implanted into PLA net, most of SC were retained in the pore of PLA net with the formation of ECM gel. SC could be adhered and grown on PLA fiber. 3. Most of SC in ECM gel could be survived to 21 days after transplantation. Survival cell numbers of SC/ECM and SC/ECM/PLA groups were obviously higher than SC suspension group. CONCLUSION Non-spinning PLA porous biodegradable materials with ECM is benefit for SC to be adhered and grown.
Objective To investigate the effect of homograft of marrow mesenchymal stem cells (MSCs) seeded onto poly-L-lactic acid (PLLA)/gelatin on repair of articular cartilage defects. Methods The MSCs derived from36 Qingzilan rabbits, aging 4 to 6 months and weighed 2.5-3.5 kg were cultured in vitroand seeded onto PLLA/gelatin. The MSCs/ PLLA/gelatin composite was cultured and transplanted into full thickness defects on intercondylar fossa. Thirty-six healthy Qingzilan rabbits were made models of cartilage defects in the intercondylar fossa. These rabbits were divided into 3 groups according to the repair materials with 12 in each group: group A, MSCs and PLLA/gelatin complex(MSCs/ PLLA/gelatin); group B, only PLLA/gelatin; and group C, nothing. At 4,8 and 12 weeks after operation, the gross, histological and immunohistochemical observations were made, and grading scales were evaluated. Results At 12 weeks after transplantation, defect was repaired and the structures of the cartilage surface and normal cartilage was in integrity. The defects in group A were repaired by the hylinelike tissue and defects in groups B and C were repaired by the fibrous tissues. Immunohistochemical staining showed that cells in the zones of repaired tissues were larger in size, arranged columnedly, riched in collagen Ⅱ matrix and integrated satisfactorily with native adjacent cartilages and subchondral bones in group A at 12 weeks postoperatively. In gross score, group A(2.75±0.89) was significantly better than group B (4.88±1.25) and group C (7.38±1.18) 12 weeks afteroperation, showing significant differences (P＜0.05); in histological score, group A (3.88±1.36) was better than group B (8.38±1.06) and group C (13.13±1.96), and group B was better than group C, showing significant differences (P＜0.05). Conclusion Transplantation of mesenchymal stem cells seeded onto PLLA/gelatin is a promising way for the treatment of cartilage defects.
Objective To review researches on bone defect repaired by different kinds of bio-derived bone. Methods The recent relevant literatures were extensively investigated. Preparation of bio-derived bone and effect of bone defect repair were reviewed.Results Theallogeneic and xenogeneic bone treated by different physicochemical method werenot only the substitution for bone but also the scaffold material co-cultured with seed cells to reconstruct tissue engineered bone. Conclusion The tissue engineered bioderived bone is a breakthrough for treatment of bone defect.
OBJECTIVE: To build the trestle of tissue engineering for skin with the collagen. METHODS: The collagen was obtained from the baby cattle hide pretreated by Na2S and elastinase and Protease M, then the collagen was dissolved in 0.5 mol/L acetic acid solution. The collagen was treated with Protease N to minimize its immunogenicity. The resulting collagen could be used to build the trestle of tissue engineering for skin because of good biocompatibility. The collagen molecular weight and structure were analyzed by SDS-PAGE. The bioactivity of trestle was tested in the experiment of the mice wound healing and the cell implantation. RESULTS: The SDS-PAGE result of the collagen treated by Protease M showed the typical spectrum of type I collagen. The built trestle was a collagen sponge matrix in which micropore size was 50-200 microns. It could accelerate wound healing and the implanted fibroblasts could proliferate well. CONCLUSION: The collagen treated by Protease N can get good biocompatibilily and is suitable for building the trestles of tissue engineering for skin with good bioactivity.